Solar Atmospheres Releases a New Process to Control Compound (White) Layer Formation During Vacuum Gas Nitriding

August 20, 2010

SOUDERTON, Pa., Aug. 20 /PRNewswire/ — Solar Atmospheres announces it has established a method of controlling the amount and depth of White layer resulting from Gas Nitriding. This procedure was accomplished following extensive testing using AISI 4140 Steel in a Solar Atmospheres Gas Nitriding Vacuum furnace. Various applications requiring Nitriding often require specific White layer limits which can now be provided by this process.

Following an initial rapid pump down to produce an Oxygen free, vacuum environment, the Nitriding cycle consisted of a pre-heat at a partial pressure of Nitrogen followed by Nitriding at a slightly positive pressure using an Ammonia/Nitrogen mixture. Many cycles were performed varying the time and gas flow parameters at temperature and the resulting White layer composition and thickness determined. The key to controlling the White layer formation was the introduction of a Boost-Diffusion technique during the Nitriding phase. Surface hardness and depth of nitride zone were then recorded from microhardness measurements and metallography . All this data was compiled to establish Nitriding procedures that provide the final desired structure in the minimum cycle time. This includes processes that produce the minimum depth or complete absence of White layer as dictated by the final application of the parts.

A complete technical paper outlining the entire program can be reviewed on our web site. Read the rest of the Technical Article.


    Contact:

    Don Jordan
    215-721-1502
    dfj@solaratm.com

SOURCE Solar Atmospheres


Source: newswire



comments powered by Disqus